PA6
EngineeringIndustrial nylon with excellent wear resistance.
WHY USE PA6
PA6 offers exceptional wear resistance and self-lubricating properties. Its high strength-to-weight ratio makes it ideal for demanding mechanical applications.
High-wear applications, gears, bearings, and industrial components.
PRINTING REFERENCE
How to Print PA6
The same STANDARD PRINT CO. reference values appear in the TDS download. They are starting points, not batch test results or a calibrated machine profile.
| Nozzle Temperature | 230-260°C |
|---|---|
| Bed Temperature | 80-120°C |
| Fan Speed | 0-30% |
| Print Speed | < 100 mm/s |
| Enclosure | Yes |
| Recovery drying after exposure | 80°C, 6h |
Validate with a calibration print and consult the printer, nozzle and build-surface guidance. For recovery drying, also check spool and dryer temperature limits.
Our filament is ready to print from an intact, sealed bag; no initial drying is needed. Reseal it in the foil bag with maintained desiccant between prints. Storage does not remove absorbed moisture.
Check storage and recovery dryingPROPERTIES
Key Characteristics
APPLICATIONS
What to Print With It
Engineering & industrial
Heavy-duty components for manufacturing environments.
Gears and bearings
Rotating components requiring wear resistance.
High-wear components
Parts subject to friction and abrasion.
HARDWARE
Compatible Printers
Enclosed + Heated Chamber
Active heating for engineering polymers like ABS, ASA, and nylons.
FREQUENTLY ASKED QUESTIONS
Common Questions About PA6
What is PA6 best used for?
High-wear applications, gears, bearings, and industrial components.
Do I need an enclosed printer for PA6?
The PA6 reference sheet calls for an enclosure. Check your printer setup and ventilation requirements.
Does PA6 need drying before printing?
STANDARD PRINT CO. filament is ready to print from an intact, sealed bag; no initial drying is needed. Reseal it in the foil bag with maintained desiccant between prints. After moisture exposure, assess recovery drying separately. Storage does not remove absorbed moisture; moisture-sensitive materials may need protected feeding while printing.
What nozzle temperature should I use for PA6?
The PA6 reference sheet lists 230-260°C. Use a suitable printer profile, check nozzle and build-surface compatibility, and calibrate for the part.
AVAILABILITY
Available Options
DIAMETERS
SIZES
COLOURS
See the product page for current colour availability.
RELATED
Other Materials in the Nylon Family
Engineering
PA12
Engineering-grade nylon with the lowest moisture absorption of any nylon polymer, excellent chemical resistance, and high impact strength. The most processable nylon for FDM printing.
Learn moreEngineering
PA6 Carbon Fibre
Carbon fibre reinforced PA6 for maximum performance.
Learn moreEngineering
PA12 Carbon Fibre
Carbon fibre reinforced PA12. Stiff and strong.
Learn moreReady to print with PA6?
Buy direct, run it through the Material Selector, or talk to us about your application.